Why Cement is grey in colour?

Reason behind the Grey color of Cement....

Have you ever got skeptical about the color of cement. Here is the reason behind the grey color of cement.

The reactions involved in this Hydration are :

Hydration of  C4AF  gives  hydration  products  that  are  similar in  many  respects  to  those  formed  from      C3A  under  comparable  conditions, though  typically  they contain  Fe3+ as well as  Al3+. An  iron (III) hydroxide gel  and calcium ferrite gel  are also  possible  products  of  C4AF  hydration. The  reactivity  of  the  pure  C4AF  is, in general,  much  slower  than  that  of  the  C3A.

  • Ferrite + gypsum + water ® ettringite + ferric aluminum hydroxide + lime
  • C4AF + 3CSH2 + 3H ® C6(A,F)S3H32 + (A,F)H3 + CH
C4AF  is responsible for the grey colour of cement.

why cement color
image source: lafargeholcim

The other reactions involved in the hydration of cement are :

Tricalcium silicate (3CaO•SiO2 = C3S)

C3S on reaction with water produces C-S-H and calcium hydroxide, CH, (also known as Portlandite). The hyphens used in the C-S-H formula are to depict its variable composition: CSH would imply a fixed composition of CaO.SiO2.H2O. C/S ratios in C-S-H vary from 1.2 to 2.0, and H/S ratios vary between 1.3 and 2.1.

    Tricalcium silicate + water ® calcium silicate hydrate + lime + heat
                 2C3S + 6H ® C3S2H3 + 3CH, D H = 120 cal/g

Dicalcium silicate (2CaO•SiO2 = C2S)

The kinetics and hydration mechanism for C2S are similar to those of C3S, except that the rate of reaction is much slower. The hydration products are the same except that the proportion of CH produced is about one-third of that obtained on hydration of C3S.

      Dicalcium silicates + water ® calcium silicate hydrate + lime
                    C2S + 4H ® C3S2H3 + CH, D H = 62 cal/g

Tricalcium aluminate (3CaO.Al2O3 = C3A)

The initial reaction of C3A with water in the absence of gypsum is vigorous, and can lead to “flash set” caused by the rapid production of the hexagonal crystal phases, C2AH8 (H = H2O) and C4AH19. Sufficient strength is developed to prevent continued mixing. The C2AH8 and C4AH19 subsequently convert to cubic C3AH6 (hydrogarnet), which is the thermodynamically stable phase at ambient temperature. Typically, gypsum is added to retard this reaction, though other chemical additives can be used.

    Tricalcium aluminate + gypsum + water ® ettringite + heat
            C3A + 3CSH2 + 26H ® C6AS3H32, D H = 207 cal/g

The reaction products formed on reaction of C3A in the presence of gypsum depend primarily on the supply of sulfate ions available from the dissolution of gypsum. The primary phase formed is ettringite (C6AS3H32) (S = SO3). Ettringite is the stable phase only as long as there is an adequate supply of soluble sulfate. A second reaction takes place if all of the soluble sulfate is consumed before the C3A has completely reacted. In this reaction, the ettringite formed initially reacts with the remaining C3A to form a tetracalcium aluminate monosulfate-12- hydrate known as monosulfate or monosulfoaluminate (C4A SH12).

    Tricalcium aluminate + ettringite + water   monosulfate aluminate hydrate
                  2C3A + 3 C6AS3H32 + 22H ® 3C4ASH18

Next Post »